Chemical Analysis of Stainless Steel Wire |
AISI/N-S Type No. |
C | Mn Max. | Si Max. | P Max. |
S Max. |
Cr | Ni | Other | |
302 |
0.15 max. | 2.00 | 1.00 | 0.045 | 0.030 | 17.00- 19.00 |
8.00- 10.00 |
N .10 max. | |
NS 18-2 | 0.15 max. | 11-14 | 1.00 | 0.060 | 0.030 | 16.50- 19.00 |
0.50- 2.50 |
N .20-.45 | |
NS 22 | 0.06 max. | 4-6 | 1.00 | 0.040 | 0.030 | 20.50- 23.50 |
11.50- 13.50 |
Mo 1.5-3.0 |
N .20-.40 V .10-.30 |
304 | 0.08 max. | 2.00 | 1.00 | 0.045 | 0.030 | 18.00- 20.00 |
8.00- 10.50 |
N .10 Max. | |
305 |
0.12 max. | 2.00 | 1.00 | 0.045 | 0.030 | 17.00- 19.00 |
10.00- 13.00 |
||
316 | 0.08 max. | 2.00 | 1.00 | 0.045 | 0.030 | 16.00- 18.00 |
10.00- 14.00 |
Mo 2.00-3.00 | |
321 | 0.08 max. | 2.00 | 1.00 | 0.045 | 0.030 | 17.00- 19.00 |
9.00- 12.00 |
Ti 5xC min. | |
347 | 0.08 max. | 2.00 | 1.00 | 0.045 | 0.030 | 17.00- 19.00 |
9.00- 13.00 |
Cb+Ta 10xC min. | |
420 |
Over 0.15 max. |
1.00 | 1.00 | 0.040 | 0.030 | 12.00- 14.00 |
|||
430 | 0.12 max. | 1.00 | 1.00 | 0.040 | 0.030 | 16.00- 18.00 |
|||
17-7 PH | 0.09 max. | 1.00 | 1.00 | 0.040 | 0.030 | 16.00- 18.00 |
6.50- 7.75 |
Al .75-1.50 |